Dense Cordierite Honeycomb Ceramic

Dense Cordierite Honeycomb Ceramic

Superior thermal shock resistance (ΔT≥300°C) with ultra-low CTE (≤3.5×10⁻⁶/K).

Key Features:

✔ Multiple cell configurations (13×13 to 60×60)

✔ Excellent thermal stability (1300°C max)

✔ High compressive strength (8-12MPa)

✔ Low water absorption (3-7%)

Applications:

• RTO systems

• Catalytic converters

• Industrial filtration

Chemical composition: 35-45% SiO₂, 45-55% Al₂O₃, 7-9% MgO

Physical Properties
Dense Cordierite Ceramic Honeycomb Structure Diagram Physical Product
Media Type	Cell Configuration
Media Type	13 Cell	15 Cell	25 Cell	32 Cell	40 Cell	43 Cell	50 Cell	60 Cell
Cell Count	13 × 13	15 × 15	25 × 25	32 × 32	40 × 40	43 × 43	50 × 50	60 × 60
Module Size (mm)	150 × 150 × 150 / 150 × 150 × 300
Shape of Terminal Face	Flat Surface / Slant / Single Slot / Dual Slots
Cell opening shape (at the end face)	Square
Cell width (mm)	9.5	8.1	4.9	3.8	3.1	2.8	2.4	2.0
Inner wall thickness (mm)	1.8	1.7	1.05	0.8	0.65	0.62	0.55	0.5
Outer wall thickness (mm)	3.2	3.1	2.2	2.2	2	2	1.8	1.8
Specific surface area (m²/m³)	315	353	568	720	891	950	1095	1276
Void Fraction (%)	66%	64%	65%	65%	65%	65%	64%	61%
Heat Capacity (J/Kg·k)	≥1100
Compressive Strength Axis A/B (MPa)	6
Compressive Strength Axis C (MPa)	10
Thermal expansion coefficient (10⁻⁶/K, 20-1000℃)	4.2-6
Thermal Conductivity (W/m·k, 20-1000℃)	1.5-2.0
Max working temperature (℃)	1300
Thermal shock resistance temperature (△T ℃)	≥350
Water absorption (%)	14-18
More sizes are available upon request.
Chemical Analysis
Chemical Composition	SiO₂	Al₂O₃	Fe₂O₃	MgO	K₂O + Na₂O + CaO
% by Weight	35-45	45-55	<1	7-9	3-5